1. PET film is a polyester film that offers excellent clarity, strength, and dimensional stability.
2. It has good chemical resistance, excellent electrical properties, and good abrasion resistance.
3. It also has a low water absorption rate and is highly resistant to UV radiation.
4. It is easy to print on, provides excellent clarity and flatness when laminated, and is an ideal material for applications that require superior optical properties.
5. PET film is also an environmentally friendly option, as it is recyclable and does not contain chlorine or other hazardous chemicals.
Product Performance Features
The white film is made of special raw materials and special processes. In addition to the good physical and chemical properties of the ordinary film, it also has:
Low light transmittance.
Good surface gloss, and an excellent shading effect.
It has good compound and printing properties.
Thickness | Width | Roll Core Inner Diameter |
50um~100um | Can Be Customized | Small:76mm Large: 152mm |
Note: Can be customized, common width is 1005mm/1035mm/1050mm/1080mm/1095mm, etc.
Project | Unit | Detection Value | Detection Method | |||
Thickness | um | 50 | 75 | 100 | GB/T13542.2 | |
Mean Thickness Deviation | um | ±3% | ||||
Tensile Strength | MD | Mpa | MD≥150 | GB/T13542.2 | ||
TD | Mpa | TD≥170 | ||||
Breaking Elongation | MD | % | 70≤MD≤180 | GB/T13542.2 | ||
TD | % | 70≤TD≤180 | ||||
Thermal Shrinkage 150'C / 30 min | MD | % | 0≤MD≤1.3 | GB/T13542.2 | ||
TD | % | -0.3≤TD≤0.3 | ||||
Transmittance | % | 88~93 | 88~93 | 88~93 | GB/T2410 | |
The Fog Degree | % | 18~25 | 18~25 | 18~25 | ||
Wetting Tension | have | mN/m | ≥56 | GB/T14216 | ||
Non | mN/m | ≥38 | ||||
Note:
1. MD means longitudinal tensile, TD meanstransverse tensile
2. The above are typical values instead of guar-antee value. Typical values can be adiusted accordIg to customers requirements
Apply in the field of white and smooth BOPET film with highlight-proofness.
Please fill in the below information if you have any questions, we will reply to you shortly.